clonesix Novice
Joined: 19 Jan 2007 Posts: 63 Location: california
|
Posted: Fri Sep 12, 2008 12:02 am Post subject: Case molds |
|
|
Since Jim was good enough to add this little section, I thought that I would add a few thoughts on the subject.
Case molds, also known as Matrix mold, blanket mold, skin mold, etc. are simple a rubber mold that is supported by a ridged shell. You could simply pour a mold with solid RTV and have a fine mold. At $100/gal for RTV, this makes for a very $$ mold. So if one could have a surface coat of RTV, backed up by a cheaper and more ridged material, it makes for a very economical product.
There are two schools of thought on this topic: 1) rubber first; case second. and 2) case first; rubber second. I am a believer in the second school for the reason that the case material, whether it be plaster or fiberglass, always shrinks more than the RTV. Therefore, it makes sense to create the case first and fill it with the rubber second.
This is done by creating a space for the RTV and building the shell over it. The space is made by protecting the model in a layer of saran wrap to protect it from the clay, and then covering it with a 1/2" of clay. Then the case is built over that. Once the case is done, the clay is removed, leaving a hollow space to be filled with the RTV.
This is better visualized with pictures
Start by mounting the model to a good solid surface such as a piece of 3/4" plywood. Don't go cheap here, whatever you mount it to must support the weight of the model, clay, being fiberglassed, or even plaster. In this case, I took some water clay and wrapped it in Saran Wrap. The clay will form a nice cradle to hold the model and the Saran Wrap will protect the model from geting the clay on it.
In order to get a good parting line from the masonite, I use a square and a pen to mark the outline of the model. Simply go around the model with the square and mark the outer most points of the model.
When you have made enough points to connect the dots you will have an outline of the model that can be cut out with a saber saw.
You will notice that the center line is level at 6.5". That is where the parting line will be. I use 1/4" masonite for the parting line, so subtract the 1/4" from the 6.5 and cut some uprights at 6.25"
Use a little hot glue and glue the uprights to the plywood
Mount the 1/4" masonite on top of the uprights
Now you have a good, solid parting line
Cover the model in Saran Wrap to protect it from the clay.
Slice up some 1/2" slabs of clay with a clay slicer. A clay slicer is simply a wire stretched between two carriage bolts. The thickness is adjusted by adding or subtracting nuts on the bolts. Two nuts is about 1/2". Add a few washers for thicker slices.
Here is the model covered with 1/2" of clay + a gasket edge. That is a lip that helps hold the rubber in the shell. The edges slope at 2-3 degrees to lock the rubber in. It also gives the rubber more of a mating surface when the mold is assembled.
You will notice two things here: the shiny surface is lacquer. The water clay MUST be sealed. Polyester resin that is used with the fiberglass HATES moisture. Give it 5-6 good coats of lacquer. Hell, 10 coats won't kill you. The second thing is the little plastic cup that is sitting upside down on the clay. I put that on the high spot to allow for a pour spout for the silicone RTV, to be added later.
Next, you need a GOOD coat of PVA for release for the fiberglass. I prefer to spray the PVA for an even coat, but it can also be brushed if you don't have a spray gun and air compressor.
Now you are ready for a fiberglass shell. Get two layers of 1.5 oz mat on and let set.
Here is a tip: If you wait until the resin gels (gets firm, but not completely hard) you can run a utility knife along the edge and trim a nice clean edge. If you wait until the fiberglass is completely hard, you will need to grind the edge with a belt sander to get a clean edge. GRINDING FIBERGLASS IS MISERABLE- AVOID AT ALL COSTS
After the first two layers have cured, add additional layers as needed. In this case, I added 3 more layers of 1.5 oz mat to get a 1/8" lay up. 1/8" is strong enough for a mold of this size. Large (heavier molds may require additional thickness.
Once gel-trimmed, and cured, you can flip it over and remove the masonite, and repeat the clay/seal/PVA process for the other side.
Once you have both sides done
You should end up with everything encased in fiberglass like this.
You are now ready to open up the case and remove clay from one half or the other, it doesn't matter which, but not both. Once open, you have the model sitting in the clay half and you need to use a tool to smooth out your parting line in the clay. Sorry that I don't have a picture for this, but the cleaner your parting line, the smaller the flashing and easier the cleanup.
Once you have a nice clean edge tooled into the clay, add some keys so the rubber registers back into the same place each time. I use acrylic hemispheres, but you can also poke depressions into the clay with a drill bit. It works the same.
Back to the fiberglass shell - clean out any remaining clay and sand out any rough or gummy spots. (if the water based clay wasn't completely sealed from moisture, some of the fiberglass resin might have not completely cured - not a problem)
Be sure to drill 1/16" holes in all the high spots of the case. this is to let air escape as it fills up with the RTV.
Now you can add the RTV.
NOTE: If you save the clay from the case, you can pound it into a block and measure the dimensions. Why? Because the volume of the clay = the volume of RTV. This is where METRIC rules! Cubic centimeters = grams of RTV (approximately) At $100/gallon, I don't like to waste any.
Do you see the tall funnel I have? This is because height = pressure. Fill the cone (keep it slender. A fat cone wastes RTV) with RTV and as it fills, it will bleed out the holes that you drilled in the case. Once they bleed out a little, plug the hole with a ball of clay. Add enough RTV so that the entire case fills and the is an inch or two left in the funnel.
NOTE: Be sure to check on the pour every once in a while until cured. If the unthinkable happens, and there is a blow out (or even a small leak) you will come back to the garage in the morning to find a VERY expensive mold of the floor.
Once cured for 24 hrs, remove the second half of the case and clean out the clay. Add a layer of Vaseline to the surface of the RTV and return the case (with the same 1/16" holes drilled for air) and pour the remaining RTV.
This should give you a good case mold that will produce many clean parts.
Last edited by clonesix on Sat Oct 04, 2008 1:26 am; edited 7 times in total |
|
Back to top |
|
|
CJanssen Expert
Joined: 17 Feb 2007 Posts: 215 Location: Beaverton OR
|
Posted: Fri Sep 12, 2008 6:55 pm Post subject: |
|
|
Nice work clonesix _________________ "What, you think your some kind of Jedi?"
Last edited by CJanssen on Sun Sep 14, 2008 9:23 pm; edited 1 time in total |
|
Back to top |
|
|
Stomper Master
Joined: 01 Oct 2005 Posts: 473 Location: Woodburn, Oregon USA
|
Posted: Sun Sep 14, 2008 7:07 pm Post subject: |
|
|
PERFECT TIMING with this subject, as I have been contemplating making my first case mold of a custom Mando helmet project I have been working on!
Excellent work, Brother!! _________________ Tony Krewson
FEAR... is not my god!! |
|
Back to top |
|
|
clonesix Novice
Joined: 19 Jan 2007 Posts: 63 Location: california
|
Posted: Sun Sep 14, 2008 11:21 pm Post subject: |
|
|
Thanks guys. I added some more photos that I found to add a little more to the explanation. I am sure that there is some over simplification here, but it gives the idea.
Stomper: The only difference with a mandalorian helmet, is that the mando helmet is open on the bottom. Therefore, mounting the helmet upright and making the rubber one piece rather than two, makes it a little easier. You end up with a 'bucket' type of mold.
This brings up another point. If anyone was wondering why there are those two vertical pieces on the ends of the fiberglass lay-up, It is for a base that allows the mold to stand up on its own. It is not essential, but very handy (for a little extra work) to have your mold stand on its own. I would think that it would be essential on a mandolorian helmet mold if you are trying to lay fibberglass into the 'bucket.' |
|
Back to top |
|
|
CJanssen Expert
Joined: 17 Feb 2007 Posts: 215 Location: Beaverton OR
|
Posted: Mon Sep 15, 2008 9:13 am Post subject: |
|
|
A couple of questions:
1. approx how much RTV did you use on this particular mold?
2. as far as doing this mold on an open on the bottom helmet...your saying I would mount it upright, go through all the steps shown with the clay and laquer, keeping it all one piece. Would I then have go back to horizontal and do the hard fiberglass shell in 2 pieces with the divider?
I am glad stomper mentioned the mando bucket because I am trying to figure out how to make that type of mold.
CJ _________________ "What, you think your some kind of Jedi?" |
|
Back to top |
|
|
Asok Newbie
Joined: 09 Nov 2006 Posts: 17
|
Posted: Mon Sep 15, 2008 1:53 pm Post subject: |
|
|
Quote: | Do you see the tall funnel I have? This is because height = pressure. Fill the cone (keep it slender. A fat cone wastes RTV) with RTV and as it fills, it will bleed out the holes that you drilled in the case. Once they bleed out a little, pluge the hole with a ball of clay. Add enough RTV so that the entire case fills and the is an inch or two left in the funnel. |
So, just the weight of the RTV pushes it into all the little places in the mold? It would seem to me, that there would be a lot of air holes. |
|
Back to top |
|
|
clonesix Novice
Joined: 19 Jan 2007 Posts: 63 Location: california
|
Posted: Mon Sep 15, 2008 9:05 pm Post subject: |
|
|
CJanssen wrote: | A couple of questions:
1. approx how much RTV did you use on this particular mold? |
I would guess 2 gallons. I guess because I don't remember. I also had to do it in multiple pours due to my scale only going to 2600g.
Somewhere in my instruction above, I mention that if you measure the clay, you can compute the volume of silicone. All the clay from one half was formed into a 6" cube. Unfortuneately, I don't have a metric ruler, but if you convert 6' = 15.24cm. So a 15.24 cube = 3540 cc.
CJanssen wrote: |
2. as far as doing this mold on an open on the bottom helmet...your saying I would mount it upright, go through all the steps shown with the clay and laquer, keeping it all one piece. Would I then have go back to horizontal and do the hard fiberglass shell in 2 pieces with the divider? |
Yes, one piece rubber, two piece shell. Mind you, that the bottom of the mold would be the bottom helmet. You would have to trim you helmet right at the edge of the mold to get the bottom of your helmet.
Are your helmet castings going to be fiberglass or resin? It would make a difference in how to approach the mold.
I personally, would make a fibergalss mold. The mando helmet doesn't really have a lot of detail or undercuts to it. Why use silicone at all?
How many of these things do you intend to make? That has a large influence on how much time and effort to put into a mold. |
|
Back to top |
|
|
clonesix Novice
Joined: 19 Jan 2007 Posts: 63 Location: california
|
Posted: Mon Sep 15, 2008 9:12 pm Post subject: |
|
|
Asok wrote: | Quote: | Do you see the tall funnel I have? This is because height = pressure. Fill the cone (keep it slender. A fat cone wastes RTV) with RTV and as it fills, it will bleed out the holes that you drilled in the case. Once they bleed out a little, pluge the hole with a ball of clay. Add enough RTV so that the entire case fills and the is an inch or two left in the funnel. |
So, just the weight of the RTV pushes it into all the little places in the mold? It would seem to me, that there would be a lot of air holes. |
Air holes? Do you mean against the model, or beneath the fiberglass shell?
Silicone is pretty dense and will flow into every crevice on the model. As mentioned above: "Be sure to drill 1/16" holes in all the high spots of the case. this is to let air escape as it fills up with the RTV. " If you look at the picture of the pour, you can see little blobs of clay on all the high spots. This is where holes were drilled in the case to let air escape and silicone to fill the entire shell.
I also vacuum degass all my silicone prior to pouring to minimize any bubbles. |
|
Back to top |
|
|
jegner Site Admin
Joined: 30 May 2003 Posts: 2144 Location: Texas, USA
|
Posted: Mon Mar 09, 2009 2:57 pm Post subject: |
|
|
Great info! Thanks for sharing! |
|
Back to top |
|
|
Deadline
Joined: 09 Feb 2011 Posts: 4
|
Posted: Tue Mar 29, 2011 9:24 am Post subject: Flicker images |
|
|
looks like the images are no longer available form flicker. Does anyone know how this it done? |
|
Back to top |
|
|
Big Al Newbie
Joined: 25 Jul 2011 Posts: 11
|
Posted: Wed Aug 24, 2011 2:53 pm Post subject: |
|
|
I'm a little late for this but I too would like to see the ref pics _________________ By Your Command
|
|
Back to top |
|
|
crashmann Guru
Joined: 27 Sep 2005 Posts: 501
|
Posted: Fri Aug 26, 2011 6:58 am Post subject: |
|
|
I've found the pictures and updated Clonesix' original post. Be sure to save a copy for yourself, since nothing on the Internet is guaranteed to be there tomorrow
Charlie
Last edited by crashmann on Sat Aug 27, 2011 12:27 am; edited 1 time in total |
|
Back to top |
|
|
Big Al Newbie
Joined: 25 Jul 2011 Posts: 11
|
Posted: Fri Aug 26, 2011 8:00 am Post subject: |
|
|
crashmann wrote: | I've found the pictures and updated Clone6' original post. Be sure to save a copy for yourself, since nothing on the Internet is guaranteed to be there tomorrow
Charlie |
Thanks Charlie that is Awesome you did that!....I'm saving them as we speak!!!!!
Al _________________ By Your Command
|
|
Back to top |
|
|
crashmann Guru
Joined: 27 Sep 2005 Posts: 501
|
|
Back to top |
|
|
Big Al Newbie
Joined: 25 Jul 2011 Posts: 11
|
Posted: Tue Aug 30, 2011 10:31 am Post subject: |
|
|
Great Link charlie thanks again! _________________ By Your Command
|
|
Back to top |
|
|
|
|
You cannot post new topics in this forum You cannot reply to topics in this forum You cannot edit your posts in this forum You cannot delete your posts in this forum You cannot vote in polls in this forum
|
Powered by phpBB © 2001, 2005 phpBB Group
|